In Inconel Anchor Bolts, the base elements are nickel and chromium. The Inconel 600 Anchor Bolts act as a joint or as a connection between components and concrete. The Inconel 601 Anchor Bolts are used in marine applications and also in applications where high-temperature resistance is required. The Inconel 625 Anchor Bolts are Anchor Bolts that have resistance to heat. These Anchor Bolts are also resistant to corrosion. They also have the characteristics of great strength.
The Inconel 718 Anchor Bolts have excellent finishing. The Inconel X-750 Anchor Bolts also have great functionalities. They also have the property of machinability. Also, they possess the property of weldability. The Incoloy 825 Anchor Bolts are durable and have good strength. The Incoloy 800HT Anchor Bolts also have excellent property as well as characteristics. The Incoloy 925 Anchor Bolts have high strength along with the property of being resistant to corrosion. Also, these Anchor Bolts are manufactured with high-quality raw materials, so that great quality products are manufactured.
| Specification | ASTM / ASME SB 166 / 164 / 425 / 166 / 446 / 574 / 472 |
| Standard |
DIN : DIN 934, DIN 931, DIN 970, DIN 933 UTS : UNEF, NPT, UNC, UNS, UNF, NPTF ISO : JIS standards, ISO 4033, ISO 4032, ANSI – American National Standards Institute ASME B18.5 ANSI B 28.2.4 1M as per defined in ASME B16.5 standard Monel Monel® Alloy 400 Stud nuts length ANSI B 18.2.4 2M as per defined in ASME B18.2.2 Monel Alloy 400 Hex nuts |
| Size | M3 - M56 | 3/6" to 2" | Custom Sizes |
| Length | 3 mm to 200 mm | Custom Sizes |
| Dimensions | DIN, ISO, ASTM, JIS, BS, GB, IS and all International Standards |
| Form | Hex, Threading, Square, Round as per Gauge Etc. |
| Threads | Unless otherwise specified, the threads shall be rolled or cut and tapped horizontally or vertically |
| Threads available | UNF, BSW, BSF, METRIC, UNC, or as required |
| Threads Configuration |
ASME B1.1 2A/3A – 2B/3B Inch Unified Threads and B1.13M 6h-6G Metric Coarse Threads |
| Certification | Dual Certified As per ASTM & ASME Codes |
| Test Certificate | As per EN 10204 / 3.1 Manufacturer Test Certificate, PED 97/23/EC Certified, Merkblatt AD 2000 W2 Certified |
| Raw materials Source | JSPL, Mukund Steel, Tata Steel, Dhamm Steel, Usha Martin,etc. |
| Packing | IN BULK: canton, pallet, Small Boxs / carton / pallet, or customer request |
| Surface Coating |
Cadmium Coating Hot Dipped Galvanizing Coating Ptfe Coated Phosphate Coating Teflon Coating Xylon Coating Zinc Coating |
| STANDARD | WERKSTOFF NR. | UNS | JIS | BS | GOST | AFNOR | EN |
| Inconel 600 | 2.4816 | N06600 | NCF 600 | NA 13 | МНЖМц 28-2,5-1,5 | NC15FE11M | NiCr15Fe |
| Inconel 601 | 2.4851 | N06601 | NCF 601 | NA 49 | XH60BT | NC23FeA | NiCr23Fe |
| Inconel 625 | 2.4856 | N06625 | NCF 625 | NA 21 | ХН75МБТЮ | NC22DNB4M | NiCr22Mo9Nb |
| Inconel 718 | 2.4668 | N07718 | - | - | - | - | - |
| Inconel X-750 | 2.4669 | N07750 | - | - | - | - | - |
| Incoloy 825 | 2.4858 | N08825 | NCF 825 | NA 16 | ЭП703 | NFE30C20DUM | NiCr21Mo |
| Incoloy 800HT | 1.4859 / 1.4876 | N08811 | NCF 800HT | NA 15(HT) | ЭИ670 | - | X8NiCrAlTi32-21 |
| Incoloy 925 | - | N09925 | NCF 925 | - | - | - | - |
| Grade | C | Mn | Si | S | Cu | Fe | Ni | Cr |
| Inconel 600 | 0.15 max | 1.00 max | 0.50 max | 0.015max | 0.50 max | 6.00 – 10.00 | 72.00 min | 14.00 – 17.00 |
| Inconel 601 | 0.10 max | 1.0 max | 0.5 max | 0.015 max | 1.0 max | Balance | 58.0 – 63.0 | 21.0 – 25.0 |
| Inconel 625 | 0.10 max | 0.50 max | 0.50 max | 0.015 max | - | 5.0 max | 58.0 min | 20.0 - 23.0 |
| Inconel 718 | 0.08 max | 0.35 max | 0.35 max | 0.015 max | 0.30 max | - | 50.00 - 55.00 | 17.00 - 21.00 |
| Incoloy X-750 | 0.08 max | 1.00 max | 0.50 max | 0.01 max | 0.50 max | 5.0 - 9.0 | 70.00 min | 14.00 - 17.00 |
| 825 | 0.05 max | 1.00 max | 0.5 max | 0.03 max | 1.50 – 3.00 | 22.00 min | 38.00 – 46.00 | 19.50 – 23.50 |
| 800HT | 0.06 – 0.10 | 1.50 max | 1.00 max | 0.015 max | 0.75 max | 39.50 min | 30.00 – 35.00 | 19.00 – 23.00 |
| 800HT | 0.03 max | 1.00 max | 0.5 max | 0.03 max | 1.5 - 3.0 | 22 min | – | 19.5 - 22.5 |
| Element | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| Inconel 600 | 8.47 g/cm3 | 1413 °C (2580 °F) | Psi – 95,000 , MPa – 655 | Psi – 45,000 , MPa – 310 | 40 % |
| Inconel 601 | 8.1 g/cm3 | 1411 °C (2571 °F) | Psi – 80,000 , MPa – 550 | Psi – 30,000 , MPa – 205 | 30 % |
| Inconel 625 | 8.4 g/cm3 | 1350 °C (2460 °F) | Psi – 1,35,000 , MPa – 930 | Psi – 75,000 , MPa – 517 | 42.5 % |
| Inconel 718 | 8.2 g/cm3 | 1350 °C (2460 °F) | Psi – 1,35,000 , MPa – 930 | Psi – 75,000 , MPa – 482 | 45 % |
| Inconel X-750 | - | 1430°C | 1267 MPa | 868 MPa | 25 % |
| 825 | 8.14 g/cm3 | 1400 °C (2550 °F) | Psi – 80,000 , MPa – 550 | Psi – 32,000 , MPa – 220 | 30 % |
| 800HT | 7.94 g/cm3 | 1385 °C (2525 °F) | Psi – 75,000 , MPa – 520 | Psi – 30,000 , MPa – 205 | 30 % |
| 925 | 8.08 g/cm3 | 1311°C-1366 °C | 685 MPa | 271 MPa | 56% |