Stainless Steel 410s Bolts are made up of martensitic steel. Their chemical composition comprises 13.5 percent of chromium and nickel along with carbon, manganese, and other elements like silicon, phosphorus, sulphur, etc. Therefore, these bolts also have resistance to wear and tear. In ordinary or in annealed conditions this material is also magnetic.
The Stainless Steel 410s Bolts are a mendable form of stainless Steel 410s Bolt, which is non-heat. These bolts are resistant to corrosion which is similar to alloy 410. These are also resistant to oxidation. Even when cooled down from above the specific temperature, 410S remains soft and ductile. This non-hardening property aids in the prevention of cracking when the alloy is subjected to highly elevated temperatures or welded. In the annealed state, UNS S41008 Bolt is entirely ferritic. It has adequate corrosion resistance, comparable to 410. Also, these bolts have good oxidation resistance.
Stainless Steel 410s Bolts are manufactured by considering all the industrial standards and guidelines along with the necessary rules and regulations required to manufacture a quality product. They could be available in different shapes, sizes, as well as dimensions, depending upon the specifications and needs of the clients or the requirement of the application. Because of their properties and characteristics they are used in a large number of industries such as Petroleum Refining and Petrochemical Processing.
| Specifications | DIN, ISO ,JIS ,GB, IS, BS, ASTM |
| Standard | ASTM / ASME SB 160 / 164 / 425 / 166 / 446 / 574 / 472 |
| Size | M0.2 to M33 | 3/6" to 2" | Custom Sizes |
| Length | 3 mm to 200 mm | Custom Sizes |
| Dimensions | DIN 931, 933, 934, 7991, 976, 125, ASME B18.2.1, B18.3 |
| Form | Hex, Threading, Square, Round as per Gauge Etc. |
| Threads | Unless otherwise specified, the threads shall be rolled or cut and tapped horizontally or vertically |
| Threads available | UNF, BSW, BSF, METRIC, UNC, or as required |
| Threads Configuration | ASME B1.1 2A/3A – 2B/3B Inch Unified Threads and B1.13M 6h-6G Metric Coarse Threads |
| Certification | Dual Certified As per ASTM & ASME Codes |
| Test Certificate | As per EN 10204 / 3.1 Manufacturer Test Certificate, PED 97/23/EC Certified, Merkblatt AD 2000 W2 Certified |
| Raw materials Source | JSPL, Mukund Steel, Tata Steel, Dhamm Steel, Usha Martin,etc. |
| Packing | IN BULK: canton, pallet, Small Boxs / carton / pallet, or customer request |
| Surface Coating |
Cadmium Coating Hot Dipped Galvanizing Coating Ptfe Coated Nickel Alloy 200 Bolts Phosphate Coating Teflon Coating Xylon Coating Zinc Coating |
| AISI Grade Equivalent | JIS Equivalent | Stainless Steel Notation | EN/DIN Numerical Equivalent | UNS designation |
EN/DIN Symbolical Equivalent |
| AISI 410S | SUS410S | SS 410S | EN 1..4516 | UNS S41008 | X6CrNiTi12 |
| Element | C | Mn | Si | P | S | Cr | Ni |
| 410S | 0.08 max | 1.00 max | 1.00 max | 0.04 max | 0.03 max | min: 11.5 max: 14.5 |
0.60 max |
| Grade | Tensile Strength ksi (MPa) min | Yield Strength 0.2% offset ksi (MPa) min | Elongation (% in 50mm) min | Hardness (Rockwell B) MAX |
|---|---|---|---|---|
| 410S | 64.4 (444) | 42 (290) | 33 | 75 |